Fatigue behaviour of composite–composite joints reinforced with cold metal transfer welded pins

In this paper the fatigue properties of through-the-thickness reinforced joints are studied in detail. Unreinforced specimens, specimens reinforced with cold metal transfer welded titanium and steel pins and specimens reinforced with titanium z-pins are investigated. Besides classical S–N diagrams, hysteresis curves and stiffness based approaches are applied to improve the understanding of the mechanical behaviour of the joints in the progress of their fatigue life. Furthermore full field strain analysis gives information about damage initiation and growth in the joint section.     

涂层工艺及参数对巧克力制品品质的影响

通过单因素和正交试验,研究了巧克力涂层温度、涂层厚度和冷却条件对巧克力涂层产品品质的影响。结果表明:巧克力冷却条件是影响巧克力涂层产品品质的首要因素,其次是涂层温度和涂层厚度。优化后最终成品巧克力涂层工艺参数是:36℃的涂层温度、0.5 mm的涂层厚度和12℃-10℃-12℃的冷却条件。     

新疆大厚度湿陷性黄土地基处理方法研究

本文介绍了新疆地区在大厚度湿陷性黄土区域地基处理方法适用性的探究,根据工程实例归纳总结了不同处理方法的优缺点,总结提出适宜的处理方法及需要考虑各种因素,为相关工程提供借鉴。     

Effects of the film thickness and poling electric field on photovoltaic performances of (Pb,La)(Zr,Ti)O3 ferroelectric thin film-based devices

The ferroelectric photovoltaic (FPV) effect obtained in inorganic perovskite ferroelectric materials has received much attention because of its large potential in preparing FPV devices with superior stability, high open-circuit voltage (V_oc) and large short-circuit current density (J_sc). In order to obtain suitable thickness for the ferroelectric thin film as light absorption layer, in which, the sunlight can be fully absorbed and the photo-generated electrons and holes are recombined as few as possible, we prepare Pb_0.93La_0.07(Zr_0.6Ti_0.4)_0.9825O₃ (PLZT) ferroelectric thin films with different layer numbers by the sol-gel method and based on these thin films, obtain FPV devices with FTO/PLZT/Au structure. By measuring photovoltaic properties, it is found that the device with 4 layer-PLZT thin film (~300 nm thickness) exhibits the largest V_oc and J_sc and the photovoltaic effect obviously depends on the value and direction of the poling electric field. When the device is applied a negative poling electric field, both the V_oc and J_sc are significantly higher than those of the device applied the positive poling electric field, due to the depolarization field resulting from the remnant polarization in the same direction with the built-in electric field induced by the Schottky barrier, and the higher the negative poling electric field, the larger the V_oc and J_sc. At a -333 kV/cm poling electric field, the FPV device exhibits the most superior photovoltaic properties with a V_oc of as high as 0.73 V and J_sc of as large as 2.11 μA/cm². This work opens a new way for developing ferroelectric photovoltaic devices with good properties.     

里必井田承压水带压开采评估

煤层底板承压水突出是发生水害事故的原因之一,要减少该类事故的发生,需对底板突水危险性进行准确评价。为保障里必井田承压水带压开采的安全进行,基于煤层底板突水研究理论分析,采用常规突水系数法和等效厚度突水系数法,分别对里必井田内3#煤和15#煤的奥灰水突水危险性进行了研究。研究发现,奥灰水对于3#煤的开采影响不大,但在局部构造及陷落柱发育地段及采区东北部区域仍存在一定的突水可能性;奥灰水对15#煤开采具有较大威胁,大部分区域具有较大突水危险性。等效岩层厚度法计算的突水系数考虑了不同性质岩层的岩石强度和阻水能力,计算更接近生产实际,结果更可靠;且在对突水系数法进一步优化后,其评价的结果可以更精确。     

辅助电流对Cu/Al大功率超声波焊接的影响

为获得更高质量的Cu/Al异质金属接头，开展了Cu/Al电流辅助大功率超声波焊接工艺试验，研究了辅助电流对Cu/Al超声波焊接的界面温度、材料塑性流动、界面中间相分布及接头力学性能的影响。结果表明，复合焊件成型良好，其接头抗拉剪力为3030 N，接头的断裂模式为韧性-脆性复合断裂。在同样的焊接时间0.2 s内，随着电流的增大，Cu/Al界面温度增加，金属塑性流动以及界面扩散也随之增强，这说明辅助电流能明显促进界面冶金；相比长时间0.4 s的超声波焊接，辅助电流能在保证界面温度、材料塑性变形的前提下，能明显减薄了界面IMC层的厚度，这是电流增强Cu/Al接头的主要物理机制。研究结果为优化Cu/Al复合焊接头强度提供了参考。     

含磷极压抗磨剂抗微点蚀性能评价和机理分析

目的 评价三种含磷极压抗磨剂的抗微点性能并分析其作用机理。方法 使用MPR模拟微点蚀试验机考察三种含磷极压抗磨剂（磷型P-1、硫磷型P-2、分散型P-3）的抗微点蚀性能。使用四球试验机、铜片腐蚀试验仪、烘箱、油膜厚度测试仪等，评价添加剂的摩擦、抗腐蚀、抗氧化性能及油膜形成能力，分析添加剂抗微点蚀性能与上述性能之间的关系。借助SEM测试分析不同添加剂的抗微点蚀机理。结果 添加P-3的润滑油GO-3的综合性能最好，GO-3具有良好的抗微点蚀性能，9 h MPR试验的辊子轨道宽度变化率为35.87%。GO-3具有良好的极压抗磨减摩性能，四球机试验测得其最大无卡咬负荷为1441.6 N，磨斑直径为0.38 mm，在试验载荷大于294 N时，其摩擦系数最低。GO-3的抗腐蚀性能良好，铜片腐蚀试验级别为1b。GO-3的氧化腐蚀性低，烘箱氧化试验中钢片评分为1分，且无油泥产生。GO-3的油膜形成能力强，60~120 ℃时弹性流体润滑油膜的厚度为371.2~153.6 nm。结论 分散型磷氮极压抗磨剂P-3化学活性适中，可以避免在摩擦表面发生严重腐蚀或剧烈摩擦化学反应，具有良好的承载、减摩、抗磨和抗微点蚀性能。     

SnO2纳米颗粒对Sn0.6Cu钎料微观组织及界面金属间化合物的影响

本文利用超声波辅助法制备了SnO2纳米颗粒增强Sn0.6Cu钎料。研究了SnO2对钎料的微观组织、熔化性能的影响，以及Cu/Sn0.6Cu-XSnO2/Cu钎焊接头界面反应产物的变化，测量了金属间化合物层的厚度和晶粒尺寸。结果表明：1.0wt.% SnO2很好的抑制了钎料中β-Sn的长大，细化了晶粒尺寸；含SnO2钎料的熔点与不含SnO2钎料熔点基本相同，但熔程明显减小；钎料熔炼过程中施加超声波可以细化晶粒，制得的钎料熔点和液相线温度也低于普通熔炼钎料。用含SnO2钎料钎焊接头界面处的IMC层更薄且晶粒尺寸更小，主要是因为SnO2纳米颗粒吸附在界面金属间化合物的晶面处阻碍铜板与钎料基体之间的相互扩散，导致IMC的形成驱动力较低，从而抑制了界面化合物的生长。     

热处理工艺对22MnB5钢铝硅镀层氧化层厚度和组织演变的影响

目的探究奥氏体化工艺对铝硅镀层氧化层厚度和微观组织的影响规律及其演变机理。方法以热浸镀Al-10%Si的22MnB5为研究对象,采用扫描电子显微镜(SEM)、辉光放电光谱仪(GD-OES)和X射线衍射仪(XRD)等仪器,观察镀层在奥氏体化过程中氧化层厚度的变化和微观组织的演变规律。结果当试样以15℃/s的速率升温到900℃后立即水淬,镀层氧化层最薄,当试样升温到900℃保温5 min后水淬,镀层氧化层出现了不同程度的开裂,镀层表面出现孔洞和脱落的现象,氧化层厚度明显增加。结论奥氏体化保温时间比奥氏体化升温速率对镀层氧化层厚度的影响更大,保温时间越长,氧渗入镀层的深度越深,氧化层越厚,奥氏体化时间的延长不利于镀层氧化层保持完整性,影响镀层对钢基体的保护功能。镀层及其氧化层的微观组织演变规律为:镀层中首先形成Al2Fe3Si3(τ1)和Fe2Al5相,随后Fe2Al5相生长并伴随FeAl2相形成,而后FeAl2+Fe2Al5相生长且有FeAl析出,随后FeAl相生长,氧化层出现孔洞,最后氧化层破裂,镀层表面孔洞增加,最终组织为FeAl2+Fe2Al5+FeAl。